Poor Wetting
Poor solderability of the pins is not acceptable as these would form unreliable joints. The brass pins have failed to wet with solder, in fact the tin plating has separated from the base material during soldering. The brass pins should have been plated with 1-2um copper before tin/lead plating. What was astonishing was the supplier of these parts said that the components were perfectly solderable !!!!!!!!!!